Minimum Values

Typical Values

Typical composition after Sintering

Code

Tensile Properties

Hardness

Density

C

Cr

Ni

Mo

Cu

Nb

Mn

Si

P

Other

Fe

Uitimate Strength Rm

Yield Strength R_p0.2

Elonga-tion A₁₀

as sintered

case hardened

Macro

Micro

Macro

Micro

MPa

MPa

%

HV10

HV10

HV10

HV10

g/cm³

wt%

wt%

wt%

wt%

wt%

wt%

wt%

wt%

wt%

wt%

wt%

17-4PH

950

660

3

320

7.6

≤0.07

15-17.5

3-5

3-5

0.15-0.45

≤1

≤1

Balance

as sintered

17-4PH

1100

950

5

370

7.6

≤0.07

15-17.5

3-5

3-5

0.15-0.45

≤1

≤1

Balance

heat-treated

316L

510

180

50

120

7.9

≥0.03

16-18

10-14

2-3

3-5

≤2

≤1

Balance

310

N₂-sintered

800

450

16

235

7.72

0.20-0.50

24-26

19-22

1.2-1.5

≤1.5

0.75-1.30

≤2.0

HV1

310

Ar-sintered

600

250

40

160

7.65

0.20-0.50

24-26

19-22

1.2-1.5

≤1.5

0.75-1.30

≤12.0

Balance

HV1

420

heat-treated

1600

1300

2

460

≥7.3

0.18-0.30

12.0-14.0

≤1.00

≤1.00

Balance

430

350

200

30

150

100

≥7.6

≤0.08

15.5-17.5

≤1

≤1

Balance

430

Good corrosion resistance against water and steam

400

750

≥7.60

0.90-1.25

16-18

≤0.60

≤0.75

2.5-3.5

≤1.0

≤1.0

≤0.040

S≤0.030

Balance

Material

Minimum Values

Typical Values

Typical composition after Sintering

Code

Tensile Properties

Hardness

Density

C

Cr

Ni

Mo

Mn

Si

P

S

Fe

Uitimate Strength Rm

Yield Strength R_p0.2

Elonga-tion A₁₀

as sintered

case hardened

Macro

Micro

Macro

Micro

MPa

MPa

%

HV10

HV10

HV10

HV10

g/cm³

wt%

wt%

wt%

wt%

wt%

wt%

wt%

wt%

wt%

1010

400

230

26

740 HV1

690 HV1

7.5

≤0.15 

0.30-.066

≤0.4

≤0.045

≤0.045

Balance

4140

as sintered

650

400

3

230

130

7.4

 0.32-0.42

0.90-1.20

0.15-0.30

Balance

4140

heat-treated

1450

1250

2

450

7.4

0.32-0.42

0.90-1.20

0.15-0.30

Balance

4605

as sintered

600

400

5

150

7.55

0.4-0.6

1.5-2.5

0.2-0.5

Balance

4605

heat-treated

1300

1100

5

390

7.55

0.4-0.6

1.5-2.5

0.2-0.5

≤1.0

Balance

1900

1500

2

600

FN02-2%

Nickel Steel

260

150

25

110

90

600

7.5

≤0.1

1.9-2.2

≤1.0

Balance

FN08-8%

Nickel Steel

380

210

15

140

90

600

7.5

≤0.1

7.5-8.5

Balance

Material

Code

Minimum Values

Typical Values

Typical composition after Sintering

Density

Permeability

μmах

Magnetic Properties

Tensile Properties

C

Cr

Ni

Mn

Si

Fe

Maximum Polarization

Js (4kA/m)

Coercivity Hc

Residual Induction Br

Ultimate Strength Rm 

Yield Strength R_P0.2

Elonga-tion A₁₀

Hardness

g/cm³

T

A/m

T

MPa

MPa

%

HV1

wt%

wt%

wt%

wt%

wt%

wt%

430

≥7.6

3311(@p=6.68 cm3)

1.335 (@p=7.68 cm3)

73 (@ p= 7.68 cm3)

0.639 (@ p= 7.68 cm3)

≥350

≥200

30

100-150

HV10

≤0.08

15.5-17.5

≤1

≤1

Balance

FeSi3

≥7.5

5215(@ p= 7.66 cm3)

1.573 (@ p= 7.66 cm3)

73 (@ p= 7.68 cm3)

1.154 (@ p= 7.66 cm3)

≥500

≥300

20

120-160

≤0.10 

2.5-3.0

Balance

FN50-50%

20Nickel Steel

≥7.6

27270 (@ p= 7.8 cm3)

1.356 (@ p = 7.8 cm3) 

10 (@ p= 7.8 cm3)

0.8 (@ p= 7.8 cm3)

≥400

≥150

20 

100-140

 ≤0.10

49.5-50.5

Balance

Pure%20 lron

≥7.8

14236(@p=7.83 cm3)

1.635 (@p=7.83 cm3)

29 (@ p= 7.83 cm3) 

1.244 (@ p= 7.83 cm3)

≥230

≥110

40

50-60

HV10

≤0.1

Balance